Product Introduction:
HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is
a new generation electrophoretic coating researched and developed
by HLS Paint (Shanghai) Co., Ltd.
|
It represents modern technology of cathodic electrophoretic coating
that is environment-friendly with high property and low cost. Such
coating does not contain heavy metal like lead, tin, cadmium and
mercury etc. It is a two-component, water-dispersed
resin,meanwhile, it took in features of previous products, and can
adapt galvanized steel sheet perfectly, almost can be applied to
foundation coating of all metal, such as: cold and hot rolled steel
sheet, galvanized steel sheet, aluminum products, zinc-aluminum
alloy sheet and stainless steel sheet etc.
|
This product features shown below:
①,Strong anti-corrosion properties, good salt spray resistance
workpiece edge
②,The bath has strong anti-shrinkage and anti-pollution ability
③,Ideal for high demand for salt spray industry, such as pipe trench,
auto chassis parts, castings
The main component Matrix resin :
Pigment: carbon black, kaolin, antirust pigment
| Solvent: alcohol ether |
Additives: surface active agent, prevent shrinkage cavity agent
|
Matrix resin: polyurethane modified epoxy resin
|
Product quality data :
| Project | Technical data | Test standard |
Resin
(HLS-1701ELB) | Black Paste (HLS-1701EG) |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±600 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| Storage stability |
No stratified state, and there were no obvious difference compared
to before storage | In 5-35 ℃ temperature 6 months |
Note: pH, conductivity measurement in the resin/pure water = 1:1
dilution
Filling tank proportion and method:
⑴ Bath preparation
Ratio:
Resin 1200.00
Paste 200.00
DI water 2000.00
Total 3400.00
⑴ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 30-36℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of
parts coated)
Construction equipment :
Cathodic electrophoretic coating construction in the
electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
If you want to learn more about HLS coating products, please
contact Sales Department of Shanghai HLS now